| Kod |
Wysokość
H mm |
Gwint
|
E mm |
Moment dokręcania |
Napięcie pracy
V |
| CT/P 30 |
30 |
M6 |
9 |
12 Nm |
750 |
| |
|
M8 |
9 |
22 Nm |
|
| |
|
M10 |
8 |
24 Nm |
|
| CT/P 35 |
35 |
M8 |
10 |
22 Nm |
750 |
| |
|
M10 |
10 |
26 Nm |
|
| CT/P 40 |
40 |
M8 |
12 |
22 Nm |
1000 |
| |
|
M10 |
13 |
24 Nm |
|
| |
|
M12 |
13 |
36 Nm |
|
| CT/P 45 |
45 |
M8 |
13 |
22 Nm |
1000 |
| |
|
M10 |
13 |
26 Nm |
|
| CT/P 50 |
50 |
M8 |
13 |
22 Nm |
1500 |
| |
|
M10 |
13 |
26 Nm |
|
| |
|
M12 |
12 |
36 Nm |
|
| CT/P 55 |
55 |
M8 |
13 |
22 Nm |
1500 |
| |
|
M10 |
17 |
26 Nm |
|
| CT/P 60 |
60 |
M8 |
17 |
22 Nm |
1500 |
| |
|
M10 |
18 |
26 Nm |
|
| |
|
M12 |
16 |
36 Nm |
|
| CT/P 65 |
65 |
M8 |
18 |
22 Nm |
1500 |
| |
|
M10 |
17 |
26 Nm |
|
| CT/P 70 |
70 |
M8 |
17 |
22 Nm |
1500 |
| |
|
M10 |
17 |
26 Nm |
|
Tworzywo / Poliester wzmacniany włóknem szklanym
Temperatura pracy/ -40° C ~ +130° C
Próba ogniowa / Klasa UL94 – VO; HL2; EN 45545-2
Wytrzymałosć mechaniczna: tolerancja +/- 10%
| TYP |
CT/P30 |
CT/P40 |
CT/P50 |
CT/P60 |
Napięcie przeskoku iskry po powierzchni
kV |
8 |
10 |
10 |
10 |
Napięcie przebicia izolatora wewnątrz
kV |
20 |
25 |
35 |
35 |
Wytrzymałość na rozciąganie
DN |
1000 |
1000 |
1000 |
1000 |
Wytrzymałość na zginanie
DN |
750 |
700 |
500 |
370 |
Wytrzymałość na ściskanie
DN |
8000 |
8000 |
8000 |
8000 |
Wytrzymałość na skręcanie
DN x mm |
3-6 |
3-6 |
3-6 |
3-6 |
1DN~1Kg